ABSTRACT
The purpose of this study was to evaluate a physical property (surface roughness) and a mechanical property (microhardness) of four type IV gypsum. 40 specimens were prepared from a metal matrix that reproduced an edentate upper alveolar ridge. They were divided into 4 groups (n = 10 Clone (G3), Durone(G4), SSWhite (G2), Asfer (G1) and submitted to roughness and microhardness tests . The obtained data were submitted to statistical analysis. By the Kolmogorov-Smirnov test it was verified that there was non-parametric distribution of the samples. The non-parametric Kruskal-Wallis and Mann-Whitney-U tests were applied in hardness and roughness data. In microhardness group 3(Clone) presented the best values (103.0 HV). In surface roughness (Ra), group 3(Clone) and Group 2 (SSWhite) showed the lowest values (1.8 µm) and all evaluated groups presented higher values than those found in metallic matrix (baseline). It was concluded that gypsum models obtained from molds with irreversible hydrocolloid are rougher than molded surface, regardless of the commercial brand. The samples made with the Clone gypsum (G3) have the highest microhardness.(AU)
O objetivo desse trabalho foi avaliar uma propriedade física (rugosidade superficial) e uma propriedade mecânica (microdureza) de quatro marcas comerciais de gesso tipo IV. Foram confeccionados 40 corpos de prova a partir de uma matriz metálica que reproduzia um rebordo alveolar superior edentado. Os mesmos foram divididos em 4 grupos (n=10), de acordo com as marcas comerciais (Clone, Durone, SSWhite, Asfer), e submetidos aos testes de rugosidade e microdureza superficial utilizando um rugosímetro e um microdurômetro respectivamente. Os dados obtidos foram computados e submetidos à análise estatística. Pelo teste de Kolmogorov-Smirnov verificou-se que não houve distribuição Normal das amostras. Dessa forma foram aplicados os testes não paramétricos de Kruskal-Wallis e Mann Whitney-U em ambas as análises. Na microdureza, a marca comercial Clone apresentou os melhores valores (103,0). Já na rugosidade superficial as marcas comerciais Clone e SSWhite apresentaram os menores valores (1,8). Ainda em relação à rugosidade superficial, as marcas comerciais avaliadas apresentaram valores maiores que os encontrados na matriz metálica. Concluiu-se que modelos em gesso obtidos a partir de moldes com hidrocolóide irreversível apresentam-se mais rugosos que a superfície moldada, independente da marca comercial avaliada. Os modelos em gesso confeccionados com a marca Clone apresentam melhor microdureza superficial. (AU)
ABSTRACT
Abstract Aim: To evaluate if gypsum mixed with different water types, with their different compositions influence the dimensional change, surface roughness and compressive strength of type IV and V gypsum specimens. Methods: Sixty specimens were fabricated from metal matrices and divided into six groups (n=10) according to the used type of gypsum and water: G1, G2 and G3 - type IV gypsum and tap, mineral and distilled water, respectively; G4, G5 and G6 - type V gypsum and tap, mineral and distilled water, respectively. Water/powder ratio followed the manufacturer's recommendations (19 mL/100 g) in all groups. The same specimens were used for all tests. A micrometer dial evaluated the dimensional change. The surface roughness of three random points was determined with a rugosimeter; a universal testing machine performed the compressive strength test. The data were subjected to analysis of variance (ANOVA). Results: There was no statistically significant difference (p>0.05) between the three types of water in the studied variables. There was statistically significant difference (p<0.05) between the gypsum mixes for the dimensional change variable. Conclusions: The different water types, with their different compositions, did not influence the analyzed physical and mechanical properties.